硅膠手板模型是重要的一種手板材料，很多產(chǎn)品中都需要用到硅膠產(chǎn)品。那么硅膠手板模型加工注意事項有那些呢？手板模型加工有氣泡、粘模及變形怎么處理呢？

Silicone hand model is an important hand material, and silicone products are needed in many products. So what are the precautions for silicone hand mold processing? How to deal with bubbles, mold sticking and deformation in the processing of hand model?

1、模具硅膠里有很多氣泡

1. There are many bubbles in the silicone of the mold

這種情況要依據(jù)條件來處里，在有抽真空機的條件下，先要把硅膠與固化劑攪拌均勻后進行抽真空處理。如沒有真空機則可以適當減少固化劑的添加量來進行處理，比如原硅膠與固化劑的比率為4%,現(xiàn)在可以改成1%-2%。這樣前期模具硅膠膠連時間就會變慢，模具中的空氣就會慢慢排出，減少氣泡。

This situation should be handled according to the conditions. Under the condition of vacuum pumping machine, the silica gel and curing agent should be stirred evenly before vacuum pumping. If there is no vacuum machine, the amount of curing agent can be appropriately reduced for treatment. For example, the ratio of original silica gel to curing agent is 4%, and now it can be changed to 1% - 2%. In this way, the silica gel bonding time of the early mold will slow down, and the air in the mold will be slowly discharged to reduce bubbles.

2、硅膠出現(xiàn)粘模

2. Silicone sticking

出現(xiàn)這種情況一是因為前期對模種（產(chǎn)品模型）沒有合理處理造成的，所以在開模前要對模種進行處理，如模種表面比較粗燥或做很復雜的模具，一定要認真打磨光滑清洗干凈。然后再均勻刷上脫模劑。常用的脫模劑有凡士林、洗潔精、液體石蠟等。實際操作中可根據(jù)模種的材質(zhì)涂刷不同的脫模劑。二是固化劑攪拌不均勻就倒入模具框中，脫模時一塊干一塊不干。

One reason for this is that there is no reasonable treatment of the mold type (product model) in the early stage, so the mold type should be treated before opening the mold. If the surface of the mold type is rough and dry or a very complex mold is made, it must be carefully polished and cleaned. Then apply the release agent evenly. Common mold release agents include Vaseline, detergent, liquid paraffin, etc. In practice, different release agents can be applied according to the material of the mold. Second, the curing agent is poured into the mold frame if it is not stirred evenly, and it will be dried one by one during demoulding.

3、硅膠模具產(chǎn)品變形

3. Silicone mold product deformation

濟南手板廠家認為這個要依據(jù)產(chǎn)品的大小來分開處理，原則上是產(chǎn)品的大小尺寸與所使用硅膠的硬度成正比。若是小件產(chǎn)品或非常精細的產(chǎn)品可以使用很軟的硅膠來開模，硬度一般在10-20度，這樣會好脫模，還不會破壞精細產(chǎn)品的紋路。

Jinan hand board manufacturers believe that this should be handled separately according to the size of the product. In principle, the size of the product is directly proportional to the hardness of the silicone used. For small products or very fine products, very soft silica gel can be used to open the mold, and the hardness is generally 10-20 degrees, which will facilitate demoulding and will not damage the lines of fine products.

若是大件產(chǎn)品比如大于50公分的產(chǎn)品就一定要使用硬度為40-50的硅膠來開模。這樣才不會變形。若是做很大而且又很精細的產(chǎn)品可以使用硬度為30度左右的硅膠來開模（方法是刷一層硅膠蒙上一層玻璃纖維布再刷一層硅膠），外面可以用石膏，玻璃鋼（即不飽和樹脂+玻璃纖維布）來做外膜，以此來保護的產(chǎn)品不變形。

For large products, such as products larger than 50 cm, silicone with a hardness of 40-50 must be used to open the mold. This will not deform. For large and fine products, you can use silica gel with a hardness of about 30 degrees to open the mold (by brushing a layer of silica gel, covering it with a layer of glass fiber cloth, and then brushing a layer of silica gel). Gypsum and glass fiber reinforced plastic (that is, unsaturated resin + glass fiber cloth) can be used as the outer film to protect the product from deformation.

以上就是問題解答的相關(guān)內(nèi)容了，希望能夠幫助到大家，如對這一問題還存在任何疑問，都歡迎關(guān)注我們網(wǎng)站http://www.ebook5.cn并咨詢我們的工作人員，將竭誠為您服務(wù)。

The above is the relevant content of the question answer. I hope it can help you. If you still have any questions about this problem, you are welcome to follow our website http://www.ebook5.cn And consult our staff, will serve you wholeheartedly.